MIM (Metal Injection Molding) :
MIM (Metal Injection Molding) is a metalworking process in which finely-powdered metal is mixed with binder material to create a “feedstock” that is then shaped and solidified using injection molding.
Plus, MIM is be used across different industries including your cell phone.
Introduction of MIM:
- The molding process allows high volume, complex parts to be shaped in a single step.
- After molding, the part undergoes conditioning operations to remove the binder (rebinding) and densify the powders. Finished products are small components used in many industries and applications.
- MIM has used to manufacture millions of parts for medical device including powered device drive chains, end effectors, connectors, and other applications. for over 20 years.
1st step: Very fine metal powders are combined with thermoplastic and wax binders in a precise recipe. A proprietary compounding process creates a homogenous pelletized feedstock that can be injection molded just like plastic. This achieves ultra-high density and close tolerances over high-production runs.
2nd Step: Unlike standard powder metallurgy, which can achieve only 80-90% of theoretical density, MIM results in 95-100%. This means we can achieve close tolerances and reduce costs by producing small, complex parts over high production runs.
3rd Step: The feedstock is heated and injected into a mold cavity under high pressure. This enables us to produce extremely complex shapes and allows for shorter cycle times.
4th Step: Once molded, the component is referred to as a “green” part. Its geometry is identical to the finished piece but is about 20% larger to allow for shrinkage during the final sintering phase.
5th Step: Binder removal (rebinding) involves a controlled process to remove most of the binders and prepare the part for the final step – sintering.
6th Step: Once rebinding is complete, the component is referred to as “brown.”
7th Step: The brown part is held together by a small amount of the binder, and is very fragile.
8th Step: Sintering eliminates the remaining binder and gives the part its final geometry and strength.
9th Step: During sintering, the part is subjected to temperatures near the melting point of the material.
Advantage of MIM:
Metal Injection Molding have excellent strength, hardened and welded and heat treated like any other wrought material.
The advantage 2H1U: